| Customization: | Available |
|---|---|
| Feature: | Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance |
| Production Process: | Casting High Temperature Firing |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Chemical and Physical Properties | SNLWB-85 | SNLWB-90 | SNLWB-95 |
| Al2O3 +MgO % min | 85 | 90 | 95 |
| Cr2O3 (C) % min | 0 | 2.5 | 2.5 |
| Apparent porosity g/cm3% max | 15 | 13 | 13 |
| Bulk density g/cm3 % min | 3.0 | 3.05 | 2.9 |
| Normal temperature Compressive strength (MPa) min | 80 | 100 | 100 |
| Breaking strength 1500°C×3hmin | 23Mpa | ||
| Chemical and Physical Properties | (Well block) | (purging plug) | |
| AL2O3 % | >=85 | >=85 | |
| MgO% | 3-5 | 1-3 | |
| Cr2O3 % | ----- | >2.4 | |
| Bulk density g\cm3 | >=3.0 | >=2.9 | |
| Apparent Porosity % | <=16 | <=18 | |
| Cold crushing strength Mpa | 110ºC*24h | >=60.0 | >=80.0 |
| 1500ºC*3h | >=100.0 | >=80.0 | |
| Refractoriness under load : ºC | >=1680 | >=1680 | |
| Modulus of rupture 1400ºC *1h Mpa Mpa | >=15.0 | >=15.0 | |
| Linear change 1500ºC*3h % | ±0.2 | ±0.2 | |
| air permeability, m3/hour at P=4 bar | 30M3/H | ||
Shandong Sinorefractory New Materials Co.,Ltd (SinoRefractory) has been focusing on international marketing of flow control refractories in iron and steel industry for 17 years.
SinoRefractory is the second generation of refractories export enterprise developed out of EMEI Group.Supported by one of China's largest production bases in functional refractory materials.
Through years of development in the field of exporting top quality refractories to worldwide markets,SinoRefractory aims at researching,producing,marketing and exporting high standard Ladle slide gate plate,Ladle Nozzles,Well blocks,Purging plugs,Nozzle stuffing sand,Refractory castables, Slide gate Mechanisms etc.
Up to now,SinoRefractory has supplied high quality refractory products and services to nearly 70 top-hundred global steel enterprises.
SinoRefractory will always put clients'interest in the first place,striving to provide a wide range of services,including technical solution,pre-sales support,after-sales services,installation team support,professional know-how according to the changing of steelmaking condition,etc.
We are not only selling products,we are more focused on supporting,developing and growing together with clients.
1. Professional in Technical Support
We have over 100 experienced technical engineers ranging from slide gates to purge plug and NFC, capable of providing comprehensive advice or solution from pre-sales to after-sales procedures.
2.Efficient in Communication
Professional and effective sales team will lower the communication cost to minimum. Getting what you need in shortest time and Supplying what you will need precisely.
3.Strict in Ouality Control
Advanced testing instruments have been set to further increase standards on pre-factory testing. We are striving to reduce the error rate below 0.01%. Making sure each product arrives at customers'warehouse in perfect condition.
4.Forty years production experience
Focusing on producing high quality slide gate refractories ever since 1983, with over 17 years experience in international trading, Fully familiar with complete procedure of exporting and importing.
5.Experienced in after-sale services
The deal is not end of our cooperation, it's just the beginning.Our services just start from cooperation, we will follow the performance and feedback of each delivery.
6.On-Site Follow up
Our team "sales+engineer" is available for on-site follow up in worldwide steel plants. With a direct visit on site, we can offer best solution to steelmakers for saving budge per ton steel.
Production&Testing Equipments:
Below are some RFQ and answers about ladle and tundish flow control refractories:
Q: What are the requirements for refractories for ladle?
A: The requirements of refractories for ladle mainly include:
* high temperature resistance
* thermal shock resistance
* resistance to the erosion of the slag
* high temperature with sufficient mechanical strength
* the lining has a certain degree of expansion
Q:What are the reasons for the destruction of refractories for ladle?
A: The main causes of damage are as follows:
When the ladle transports high-temperature molten steel, the high-temperature molten steel and slag at about 1680ºC scour and erode it, especially in the slag line part, the scouring and erosion is more serious, and it is an important factor to decide the service life of the ladle.
LF and other extra-oven refining treatment on the unburnt brick damage is serious.
Q:What steel grades are different materials of slide plate bricks suitable for respectively?
A: Different materials of slide plate bricks are applicable to different steel grades. For example,
Al2O3-ZrO2-C slide gate plate can be used as ladle sliding gate plate due to its excellent erosion resistance and thermal shock stability, which can adapt to the casting of various steel grades, and ther are the following materilas based on customer's steel making condition: the MgO-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, and so on.
For more details, feel free to send inquiry to us.