| Customization: | Available |
|---|---|
| Feature: | Chemical Corrosion Resistance, Corrosion Resistance, Good Abrasion Resistance, Good Insulation Performance, High Mechanical Strength, High Melting Point, Thermal Shock Resistance |
| Production Process: | Sintering Method |
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Raw Material | tabular corundum, fused alumina, fused alumina zirconia, zirconium mullite |
| Forming technology |
through the addition of moderate micro and fine metal powder, by reaction under high temperature, to increase the high temperature performance of plates.
Through the adding of moderate boron carbide powder to increase the oxidation resistance of plates.
The bonding agent is phenolic resin with high solid content and high carbon residue.
|
| Heat treatment technology | After forming, adopting advanced heating treatment technology, through impregnating, burning to form high performance slide plates. |
| Characteristic | With features of good thermal stability, excellent erosion resistance, stable consistency in shape and size. |
| Applicable | Mainly suitable for ladles over 180 tons or converter slagging slide gate systems. |
Technical Parameter(Chemical and Physical):
| Al2O3 | 71% | 86% | ||
| ZrO2 | 7.5% | / | ||
| C | 10% | 3% | ||
| Bulk Density | 3.1g/cm3 | 3.0g/cm3 | ||
| Apparent Porosity | 7% | 10% | ||
| CCS | 140 Mpa | 110 Mpa |