Refractory Safflow Slide Gate Set with Long Service Life

• Customization: Available
• Classification: High-Alumina
• Feature: Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity
• Model NO.: SAFFLOW
• Production Process: Pressing Methord
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Plate
• Product Name: Refractory Safflow Slide Gate Set with Long Servic
• Al2O3: 85% Min
• Apparent Porosity: 15%
• Bulk Density: 3GM./Cc Min
• C.C.S: 100MPa Min
• Application: Steel Mill Ladle
• Mould: According to The Customer′s Request
• Function: Steel Metal Molten Flow Control
• Drawing: Customized
• Chemical Physical Analysis: Customized
• Sample Order: Acceptable
• Service Life: 4-8 Heats
• Main Material: Tabular Alumina, Carbonaceous Material
• Zirconia: Can Be Added
• Type: Alumina Carbon Refractory
• Transport Package: Wooden Case
• Specification: ISO9001
• Trademark: SNREF
• Origin: Shandong Province, China
• HS Code: 69032000
• Production Capacity: 30 000 Tons/Month

Product Description

Product Description

Refractory SAFFLOW Slide Gate Set with Long Service Life
SNREF Slide Gate Plate adopts High quality bauxite material , also takes tabular alumina, carbonaceous material and zirconia-containing material as main raw materials, adds in high performance antioxidants, uses phenolic resin as binder, formed under high-pressure and burned under high temperature. The slide plates have the advantages of high strength, good erosion resistance, thermal shock resistance and good stability etc., mainly used in large and medium-sized ladle.
 

The Safflow Ladle slide gate set is widely used in various steelmaking processes, including converter steelmaking and electric arc furnace steelmaking. It is suitable for steel enterprises of different scales. Whether it is a large integrated steel plant or a small special steel plant, it can provide a reliable solution for their continuous casting production.

 

Our Advantages

Refractory SAFFLOW Slide Gate Set with Long Service Life

High Refractory Performance: Made of high-quality refractory materials, it can withstand high temperatures up to [specific temperature] °C, effectively resisting the erosion and scouring of molten steel and extending the service life.

Excellent Wear Resistance: The special formula and manufacturing process endow the product with excellent wear resistance. Even during frequent sliding operations, it can maintain good surface quality and dimensional accuracy.

Good Thermal Stability: It has good thermal stability and can prevent phenomena such as cracking or spalling under working conditions with sudden temperature changes, ensuring the continuity and safety of production.

Precise Dimensional Accuracy: Strict production control ensures the dimensional accuracy of the product, making the fit between the ladle slide gate plates tighter and effectively preventing the leakage of molten steel.

Easy Installation and Maintenance: The product has a reasonable design and a compact structure, making it easy to install and disassemble. At the same time, the maintenance cost is low, which can effectively improve production efficiency.

Detailed Photos

 

Product Parameters

Chemical and Physical Properties	Ladle Slide Gate Plate (General)
	Magnesia material	Al-C	Al- Zr-C
apparent porosity  %  max	10	8	8
Bulk Density   g/cm3  min	3.0	3.05	3.1
Compressive strength   MPa   min	120	120	120
Al2O3  %   min	8	85	85
ZrO2   %   min			4
C    %    min	3	3	3
MgO   %	65 min
Service Life  heats	1-2	1-3	1-5

Packaging & Shipping

Service Result for slide gate plate and nozzle system:
Service life depends on many points:
1)Different Raw Material,
2)Production Process(Firing temperature, oil immersion, drying temperature...)
3)Steel type
4)Steel making condition
5)Different operation mode
And so on...

 

Company Profile

Shandong Sinorefractory New Materials Co.,Ltd (SinoRefractory)has been focusing on international marketing of flow control refractories in iron and steel industry for 17 years.

SinoRefractory is the second generation of refractories export enterprise developed out of EMEI Group.Supported by one of China's largest production bases in functional refractory materials.

Through years of development in the field of exporting top quality refractories to worldwide markets,SinoRefractory aims at researching,producing,marketing and exporting high standard Ladle slide gate plate,Ladle Nozzles,Well blocks,Purging plugs,Nozzle stuffing sand,Refractory castables, Slide gate Mechanisms etc.

Up to now,SinoRefractory has supplied high quality refractory products and services to nearly 70 top-hundred global steel enterprises.

SinoRefractory will always put clients'interest in the first place,striving to provide a wide range of services,including technical solution,pre-sales support,after-sales services,installation team support,professional know-how according to the changing of steelmaking condition,etc.

We are not only selling products,we are more focused on supporting,developing and growing together with clients.

Application

Ladle Refractory Slide Gate Plate in Steel Mill Pant, for flow control the steel molten.

FAQ

Below are some FAQ and answers about ladle and tundish flow control refractories:

Q: What are the requirements for refractories for ladle?
A: The requirements of refractories for ladle mainly include: 
 * high temperature resistance
 * thermal shock resistance
 * resistance to the erosion of the slag
 * high temperature with sufficient mechanical strength
 * the lining has a certain degree of expansion

Q:What are the reasons for the destruction of refractories for ladle?
A: The main causes of damage are as follows:
When the ladle transports high-temperature molten steel, the high-temperature molten steel and slag at about 1680ºC scour and erode it, especially in the slag line part, the scouring and erosion is more serious, and it is an important factor to decide the service life of the ladle.
LF and other extra-oven refining treatment on the unburnt brick damage is serious.

Q:What steel grades are different materials of slide plate bricks suitable for respectively?
A: Different materials of slide plate bricks are applicable to different steel grades. For example, 
Al2O3-ZrO2-C slide gate plate can be used as ladle sliding gate plate due to its excellent erosion resistance and thermal shock stability, which can adapt to the casting of various steel grades, and ther are the following materilas based on customer's steel making condition: the MgO-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, MgO-Al-C, and so on.
 
 
For more details, feel free to send inquiry to us.