| Customization: | Available |
|---|---|
| Classification: | High-Alumina |
| Feature: | Good Mechanical Strength, Good Thermal Insulation Performance, High-Temperature Resistant, Low Thermal Conductivity, Instant Materials |
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
Payment Guarantee
Platform-protected payments with refund support for eligible order issues.
Platform Logistics
Inspection Service
After-Sales & Dispute Handling
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Technology Description:
Deep burnt Alumina Zirconia Carbon Slide Plate| Raw material | Tabular corundum, fused alumina, fused alumina zirconia, zirconium mullite |
| Forming technology | Through the addition of moderate micro and fine metal powder, by reaction under high temperature, to increase the performance of plates under h igh temp. Through adding of moderate boron carbide powder to increase the oxidation resistance of plates. The bonding agent is phenolic resin with high solid content and high carbon residue. |
| Heat treatment technology | After forming, adopting advanced heating treatment technology, through graphite immersion, high temperature burning to form high strength slide plates. |
| Characteristic | With features of good thermal stability, excellent erosion resistance, stable consistency in shape and size. |
| Application | Suitable for ladles over 180 tons or converter slagging slide gate systems. |
| Al2O3 | 71% |
| ZrO2 | 7.8% |
| SiO2 | |
| C | 10% |
| Bulk Density | 3.1g/cm3 |
| Apparent Porosity | 6-9% |
| CCS | 150 Mpa |
| Workmanship | Casting | Pressed |
| Al2O3 | 93% | 80% |
| ZrO2 | - | |
| SiO2 | - | |
| C | - | 3% |
| Bulk Density | 3.1g/cm3 | 2.85g/cm3 |
| Apparent Porosity | 20% | 14% |
| CCS | - | - |